Glass, Borosilicate ("Pyrex")
ASCII format ________________________________________
Energy μ/ρ μen/ρ
(MeV) (cm2/g) (cm2/g)
________________________________________
1.00000E-03 3.164E+03 3.155E+03
1.03542E-03 2.887E+03 2.879E+03
1.07210E-03 2.634E+03 2.627E+03
11 K 1.07210E-03 2.800E+03 2.790E+03
1.50000E-03 1.152E+03 1.148E+03
1.55960E-03 1.037E+03 1.033E+03
13 K 1.55960E-03 1.079E+03 1.073E+03
1.69350E-03 8.629E+02 8.583E+02
1.83890E-03 6.883E+02 6.845E+02
14 K 1.83890E-03 1.776E+03 1.723E+03
2.00000E-03 1.500E+03 1.457E+03
3.00000E-03 5.123E+02 5.011E+02
3.60740E-03 3.098E+02 3.036E+02
19 K 3.60740E-03 3.133E+02 3.067E+02
4.00000E-03 2.355E+02 2.307E+02
5.00000E-03 1.260E+02 1.235E+02
6.00000E-03 7.500E+01 7.337E+01
8.00000E-03 3.269E+01 3.178E+01
1.00000E-02 1.705E+01 1.642E+01
1.50000E-02 5.217E+00 4.828E+00
2.00000E-02 2.297E+00 1.995E+00
3.00000E-02 7.987E-01 5.684E-01
4.00000E-02 4.341E-01 2.361E-01
5.00000E-02 3.022E-01 1.235E-01
6.00000E-02 2.417E-01 7.648E-02
8.00000E-02 1.890E-01 4.230E-02
1.00000E-01 1.657E-01 3.209E-02
1.50000E-01 1.389E-01 2.727E-02
2.00000E-01 1.246E-01 2.757E-02
3.00000E-01 1.069E-01 2.885E-02
4.00000E-01 9.540E-02 2.946E-02
5.00000E-01 8.696E-02 2.957E-02
6.00000E-01 8.035E-02 2.941E-02
8.00000E-01 7.052E-02 2.868E-02
1.00000E+00 6.337E-02 2.774E-02
1.25000E+00 5.667E-02 2.650E-02
1.50000E+00 5.160E-02 2.533E-02
2.00000E+00 4.447E-02 2.337E-02
3.00000E+00 3.611E-02 2.069E-02
4.00000E+00 3.140E-02 1.904E-02
5.00000E+00 2.838E-02 1.795E-02
6.00000E+00 2.632E-02 1.721E-02
8.00000E+00 2.373E-02 1.629E-02
1.00000E+01 2.223E-02 1.579E-02
1.50000E+01 2.045E-02 1.522E-02
2.00000E+01 1.982E-02 1.503E-02
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||